samples.xml

   1 <samples xmlns="tag:fenglich.fastmail.fm,2007:Pottery" xmlns:xlink="http://www.w3.org/1999/xlink" xmlns:db="http://docbook.org/ns/docbook">
   2     <sample date="2007-09-28" xml:id="W1">
   3         <brushon idref="SandBrown"/>
   4         <clayref idref="WSW"/>
   5         <db:para>The glaze dried very quickly. Thick layer. As can be seen, a gold/lighter brown goes through, when thickness increases.</db:para>
   6     </sample>
   7     <sample date="2007-09-28" xml:id="T5">
   8         <brushon idref="SandBrown"/>
   9         <clayref idref="SaintThomas"/>
  10         <db:para>The glaze dried very quickly. Thick layer. As can be seen, a gold/lighter brown goes through, when thickness increases.</db:para>
  11     </sample>
  12     <sample date="2007-09-28" xml:id="W10">
  13         <brushon idref="ImagineGreen"/>
  14         <clayref idref="WSW"/>
  15         <db:para>Convenient thickness for brushing. Note the brown spots. Miss coloring, oven accident?</db:para>
  16     </sample>
  17     <sample date="2007-09-28" xml:id="T8">
  18         <brushon idref="ImagineGreen"/>
  19         <clayref idref="SaintThomas"/>
  20         <db:para>Convenient thickness for brushing. Note the brown spots. Miss coloring, oven accident?</db:para>
  21     </sample>
  22     <sample date="2007-09-28" xml:id="W12">
  23         <glazing sieved="no" idref="FrostedJade" hydrometerGravity="53"/>
  24         <clayref idref="WSW"/>
  25         <db:para>Very thick. Very hard to stir, could it be the temperature?</db:para>
  26     </sample>
  27     <sample date="2007-09-28" xml:id="T41">
  28         <glazing sieved="no" idref="FrostedJade" hydrometerGravity="53"/>
  29         <clayref idref="SaintThomas"/>
  30         <db:para>Very thick. Very hard to stir, could it be the temperature?</db:para>
  31     </sample>
  32     <sample date="2007-09-28" xml:id="W6">
  33         <brushon idref="GreyAmaco"/>
  34         <clayref idref="WSW"/>
  35         <db:para/>
  36     </sample>
  37     <sample date="2007-09-28" xml:id="W11">
  38         <brushon idref="GreyAmaco"/>
  39         <clayref idref="WSW"/>
  40         <db:para>Had an extra layer on the second level.</db:para>
  41     </sample>
  42     <sample date="2007-09-28" xml:id="T4">
  43         <brushon idref="GreyAmaco"/>
  44         <clayref idref="SaintThomas"/>
  45         <db:para/>
  46     </sample>
  47     <sample date="2007-09-28" xml:id="T17">
  48         <glazing idref="FrostedJade" sieved="60" hydrometerGravity="46"/>
  49         <clayref idref="SaintThomas"/>
  50         <db:para>Dipped, three seconds.</db:para>
  51     </sample>
  52     <sample date="2007-09-28" xml:id="W2">
  53         <glazing idref="FrostedJade" sieved="60" hydrometerGravity="46"/>
  54         <clayref idref="WSW"/>
  55         <db:para>Dipped, three seconds.</db:para>
  56     </sample>
  57     <sample date="2007-09-28" xml:id="T9">
  58         <glazing idref="GreenHue" sieved="60" hydrometerGravity="40"/>
  59         <clayref idref="SaintThomas"/>
  60         <db:para>Dipped, three seconds.</db:para>
  61     </sample>
  62     <sample date="2007-09-28" xml:id="W3">
  63         <glazing idref="GreenHue" sieved="60" hydrometerGravity="40"/>
  64         <clayref idref="WSW"/>
  65         <db:para>Dipped, three seconds.</db:para>
  66     </sample>
  67     <sample date="2007-09-28" xml:id="T34">
  68         <!-- Although my paper note said T31 -->
  69         <glazing idref="FrostedJade" sieved="60" hydrometerGravity="45"/>
  70         <glazing idref="GreenHue" sieved="60" hydrometerGravity="41"/>
  71         <clayref idref="SaintThomas"/>
  72         <db:para>Frosted Jade across whole, with Green Hue on top at the right corner, diagonal.</db:para>
  73     </sample>
  74     <sample date="2007-09-28" xml:id="W8">
  75         <glazing idref="FrostedJade" sieved="60" hydrometerGravity="45"/>
  76         <glazing idref="GreenHue" sieved="60" hydrometerGravity="41"/>
  77         <clayref idref="WSW"/>
  78         <db:para>Frosted Jade across whole, with Green Hue on top at the right corner, diagonal.</db:para>
  79     </sample>
  80     <sample date="2007-09-28" xml:id="W13">
  81         <glazing sieved="no" idref="WhiteGloss" hydrometerGravity="35"/>
  82         <clayref idref="WSW"/>
  83         <db:para/>
  84     </sample>
  85     <sample date="2007-09-28" xml:id="T32">
  86         <glazing sieved="no" idref="WhiteGloss" hydrometerGravity="35"/>
  87         <clayref idref="SaintThomas"/>
  88         <db:para/>
  89     </sample>
  90     <sample date="2007-09-28" xml:id="T6">
  91         <brushon idref="YellowBO"/>
  92         <clayref idref="SaintThomas"/>
  93         <db:para/>
  94     </sample>
  95     <sample date="2007-09-28" xml:id="W5">
  96         <brushon idref="YellowBO"/>
  97         <clayref idref="WSW"/>
  98         <db:para/>
  99     </sample>
 100     <sample date="2007-08-15" xml:id="T7">
 101         <glazing sieved="no" idref="FrostedJade" hydrometerGravity="46"/>
 102         <clayref idref="SaintThomas"/>
 103         <db:para>2 seconds dipping.</db:para>
 104     </sample>
 105     <sample date="2007-08-15" xml:id="T12">
 106         <glazing sieved="no" idref="FrostedJade" hydrometerGravity="46"/>
 107         <clayref idref="SaintThomas"/>
 108         <db:para>4 seconds dipping.</db:para>
 109     </sample>
 110     <sample date="2007-08-15" xml:id="T13">
 111         <glazing sieved="no" idref="GreenHue" hydrometerGravity="46"/>
 112         <clayref idref="SaintThomas"/>
 113         <db:para>2 seconds dipping.</db:para>
 114     </sample>
 115     <sample date="2007-08-15" xml:id="T10">
 116         <glazing sieved="no" idref="GreenHue" hydrometerGravity="46"/>
 117         <clayref idref="SaintThomas"/>
 118         <db:para>4 seconds dipping.</db:para>
 119     </sample>
 120     <sample date="2007-08-15" xml:id="T3">
 121         <glazing sieved="no" idref="WhiteGloss" hydrometerGravity="45"/>
 122         <clayref idref="SaintThomas"/>
 123         <db:para>2 seconds dipping.</db:para>
 124     </sample>
 125     <sample date="2007-08-15" xml:id="T2">
 126         <glazing sieved="no" idref="WhiteGloss" hydrometerGravity="45"/>
 127         <clayref idref="SaintThomas"/>
 128         <db:para>4 seconds dipping.</db:para>
 129     </sample>
 130     <!-- TODO these are weird, probably gone.
 131     <sample date="2007-09-25">
 132         <tile xml:id="T9"/>
 133         <glazing sieved="no" idref="FrostedJade"/>
 134         <db:para/>
 135     </sample>
 136
 137     <sample date="2007-09-25">
 138         <tile xml:id="W3"/>
 139         <glazing sieved="no" idref="FrostedJade"/>
 140         <db:para/>
 141     </sample>
 142     -->
 143     <sample date="2007-09-25" xml:id="W9">
 144         <!-- TODO where's the note for this sample? -->
 145         <glazing sieved="no" idref="GreenHue"/>
 146         <clayref idref="WSW"/>
 147         <db:para/>
 148     </sample>
 149     <sample date="2007-09-25" xml:id="T19">
 150         <!-- TODO where's the note for this sample? -->
 151         <glazing sieved="no" idref="GreenHue"/>
 152         <clayref idref="SaintThomas"/>
 153         <db:para/>
 154     </sample>
 155     <sample date="2007-10-29" xml:id="T40">
 156         <glazing sieved="no" idref="WhiteGloss" hydrometerGravity="50"/>
 157         <clayref idref="SaintThomas"/>
 158         <db:para>Even though the glaze is very thick, it looks sane. Only bad indication of thickness can be seen on W7 where a tiny empty spot can be seen. Maybe it could have been avoided by polishing.</db:para>
 159     </sample>
 160     <sample date="2007-10-29" xml:id="W7">
 161         <glazing sieved="no" idref="WhiteGloss" hydrometerGravity="50"/>
 162         <clayref idref="WSW"/>
 163         <db:para>Even though the glaze is very thick, it looks sane. Only bad indication of thickness can be seen on W7 where a tiny empty spot can be seen. Maybe it could have been avoided by polishing.</db:para>
 164     </sample>
 165     <sample date="2007-10-29" xml:id="T31">
 166         <glazing sieved="no" idref="WhiteGloss" hydrometerGravity="44"/>
 167         <clayref idref="SaintThomas"/>
 168         <db:para>It's dipped three times but it doesn't really show. That's good, since it means dipping time is less of a factor.</db:para>
 169     </sample>
 170     <sample date="2007-10-29" xml:id="T36">
 171         <glazing sieved="no" idref="IntenseBlack" hydrometerGravity="50"/>
 172         <clayref idref="SaintThomas"/>
 173         <db:para>Despite being very thick, it is very elegant. Doesn't move at all, when judging from other pieces.</db:para>
 174     </sample>
 175     <sample date="2007-10-29" xml:id="W4">
 176         <glazing sieved="no" idref="IntenseBlack" hydrometerGravity="50"/>
 177         <clayref idref="WSW"/>
 178         <db:para>Despite being very thick, it is very elegant. Doesn't move at all, when judging from other pieces.</db:para>
 179     </sample>
 180     <sample date="2007-11-04" xml:id="T43">
 181         <clayref idref="SaintThomas"/>
 182         <db:para>No glaze, used pens. Top, top left, and left side is with a ballpoint pen, while the bottom right is with a black lead pencil. As the tile shows there's no trace, except for the mechanical marks that the ball pen did.</db:para>
 183     </sample>
 184     <sample date="2007-11-04" xml:id="T46">
 185         <glazing sieved="no" idref="WhiteGloss" hydrometerGravity="44"/>
 186         <clayref idref="SaintThomas"/>
 187         <db:para>Drew with black lead graphite pencil, and then glazed on top of that. As the tile shows there's not a single trace, so using pen is ok.</db:para>
 188     </sample>
 189     <sample date="2007-11-04" xml:id="T44">
 190         <glazing sieved="no" idref="IntenseBlack" hydrometerGravity="42"/>
 191         <clayref idref="SaintThomas"/>
 192         <db:para>Too thin.</db:para>
 193     </sample>
 194     <sample date="2007-11-04" xml:id="T55">
 195         <glazing sieved="no" idref="IntenseBlack" hydrometerGravity="42"/>
 196         <glazing sieved="no" idref="WhiteGloss" hydrometerGravity="44"/>
 197         <clayref idref="SaintThomas"/>
 198         <db:para>White black diagonally across the tile. Both glazes to thin, or at least to quick dipping.</db:para>
 199     </sample>
 200     <sample date="2007-11-07" xml:id="T54">
 201         <brushon idref="AxnerBlackUnderGlazePen"/>
 202         <clayref idref="SaintThomas"/>
 203         <db:para/>
 204     </sample>
 205     <sample date="2007-11-07" xml:id="T33">
 206         <glazing idref="Transparent" sieved="no" hydrometerGravity="42"/>
 207         <clayref idref="SaintThomas"/>
 208         <db:para/>
 209     </sample>
 210     <sample date="2007-11-07" xml:id="T30">
 211         <glazing idref="TransparentYellowStain" hydrometerGravity="42" sieved="no"/>
 212         <clayref idref="SaintThomas"/>
 213         <db:para>Kinda ok, but it's a pity that the yellow is cold, even though Saint Thomas has a tad of iron.</db:para>
 214         <db:para>Dropped it in the floor on <db:date>2007-11-17</db:date>, glued it with cyanoacrylate glue.</db:para>
 215     </sample>
 216     <sample date="2007-11-07" xml:id="T51">
 217         <glazing idref="TransparentCopperCarbonate" hydrometerGravity="42" sieved="no"/>
 218         <clayref idref="SaintThomas"/>
 219         <db:para>Visible white spots on the sample. As if the transparent hadn't dissolved. Looks cool, annoying small spots, caused by gas extrusion? The clear metal feel to it might be avoided with less oxide, maybe.</db:para>
 220     </sample>
 221     <sample date="2007-11-10" xml:id="T47">
 222         <glazing idref="Chocolate" hydrometerGravity="42" sieved="no"/>
 223         <clayref idref="SaintThomas"/>
 224         <db:para>This is traditional dark chocolate, both in texture and color. Doubt more stain will turn this black.</db:para>
 225     </sample>
 226     <sample date="2007-11-22" xml:id="T35">
 227         <glazing idref="FrostedJade" hydrometerGravity="50" sieved="no"/>
 228         <clayref idref="SaintThomas"/>
 229         <db:para>Maybe mixed up with T42.</db:para>
 230     </sample>
 231     <sample date="2007-11-22" xml:id="T92">
 232         <glazing idref="FrostedJade" hydrometerGravity="44" sieved="no"/>
 233         <clayref idref="SaintThomas"/>
 234         <db:para>Maybe mixed up with T35. The backside reads 92.</db:para>
 235     </sample>
 236     <sample date="2007-11-22" xml:id="T39">
 237         <glazing idref="FrostedJade" hydrometerGravity="44" sieved="no"/>
 238         <glazing idref="GreenHue" hydrometerGravity="45" sieved="no"/>
 239         <clayref idref="SaintThomas"/>
 240         <db:para>Green Hue is on top, at the bottom. So Frosted Jade was applied first, in other words. Frosted Jade was dried a bit first, but not completely, since the bisque was a tad cold.</db:para>
 241     </sample>
 242     <sample date="2007-11-22" xml:id="T42">
 243         <glazing idref="FrostedJade" hydrometerGravity="44" sieved="no"/>
 244         <glazing idref="GreenHue" hydrometerGravity="45" sieved="no"/>
 245         <clayref idref="SaintThomas"/>
 246         <db:para>The opposite of T39. Frosted Jade is on top, at the bottom. So Green Hue was applied first, in other words. Green Hue was thoroughly dried with hot air gun.</db:para>
 247     </sample>
 248     <sample date="2007-11-24" xml:id="T02">
 249         <!-- T32. -->
 250         <glazing idref="GreenHueAndFrostedJade" hydrometerGravity="45" sieved="no"/>
 251         <clayref idref="SaintThomas"/>
 252         <db:para>Green Hue were on 45, Frosted Jade on 44.</db:para>
 253     </sample>
 254     <sample date="2007-11-24" xml:id="T37">
 255         <brushon idref="AmacoWhiteBO"/>
 256         <clayref idref="SaintThomas"/>
 257         <db:para>Convenient thickness. Brushed three different thickness.</db:para>
 258     </sample>
 259     <sample date="2007-11-24" xml:id="T50">
 260         <brushon idref="RedBO"/>
 261         <clayref idref="SaintThomas"/>
 262         <db:para>Brushed three different thickness.</db:para>
 263     </sample>
 264     <sample date="2007-11-27" xml:id="T72">
 265         <glazing sieved="no" idref="Transparent"/>
 266         <clayref idref="SaintThomas"/>
 267         <db:para>Applied is a slip consisting only of dilluted clay, namely, PRNF 4005 from Cerama Collet S.a, WBB Fuchs GmbH &amp; Co. Applied the slip directly after having cut out the sample, didn't wait. The glazed part is brown, tilting towards (khaki) green.</db:para>
 268     </sample>
 269     <sample date="2007-11-27" xml:id="T63">
 270         <glazing sieved="no" idref="Transparent"/>
 271         <clayref idref="SaintThomas"/>
 272         <db:para>Applied is a porcelain slip. Except for the last layer, the slip was applied directly after having cut out the sample, didn't wait. The transparent glaze turned out really well, think I dipped it for a long time.</db:para>
 273     </sample>
 274     <sample date="2007-11-27" xml:id="T56">
 275         <brushon idref="AmacoWaxyWhite"/>
 276         <clayref idref="SaintThomas"/>
 277         <db:para>Easy to brush with. The last layer was thoroughly dried before applying. 56 is scratched on the back.</db:para>
 278     </sample>
 279     <sample date="2007-12-05" xml:id="T61">
 280         <brushon idref="TurquoiseBO"/>
 281         <clayref idref="SaintThomas"/>
 282         <db:para/>
 283     </sample>
 284     <sample date="2007-12-05" xml:id="T70">
 285         <brushon idref="WhiteBO"/>
 286         <clayref idref="SaintThomas"/>
 287         <db:para/>
 288     </sample>
 289     <sample date="2007-12-05" xml:id="T60">
 290         <brushon idref="IndigoBlue"/>
 291         <clayref idref="SaintThomas"/>
 292         <db:para/>
 293     </sample>
 294     <sample date="2007-12-05" xml:id="T62">
 295         <brushon idref="OilSpot"/>
 296         <clayref idref="SaintThomas"/>
 297         <db:para/>
 298     </sample>
 299     <sample date="2007-12-05" xml:id="T69">
 300         <brushon idref="TexturedBlue"/>
 301         <clayref idref="SaintThomas"/>
 302         <db:para/>
 303     </sample>
 304     <sample date="2007-12-05" xml:id="T67">
 305         <brushon idref="GoldBrownBO"/>
 306         <clayref idref="SaintThomas"/>
 307         <db:para/>
 308     </sample>
 309     <sample date="2007-12-09" xml:id="T66">
 310         <brushon idref="VelourBlackBO"/>
 311         <glazing sieved="no" hydrometerGravity="42" idref="Transparent"/>
 312         <clayref idref="SaintThomas"/>
 313         <db:para>Four layers.</db:para>
 314     </sample>
 315     <sample date="2007-12-09" xml:id="T65">
 316         <brushon idref="CeradelNoir"/>
 317         <glazing sieved="no" hydrometerGravity="42" idref="Transparent"/>
 318         <clayref idref="SaintThomas"/>
 319         <db:para>Four layers. Extremely thick, like semi-dry tooth paste.</db:para>
 320     </sample>
 321     <sample date="2007-12-09" xml:id="T68">
 322         <brushon idref="AmacoWhiteUnderglaze"/>
 323         <glazing sieved="no" hydrometerGravity="42" idref="Transparent"/>
 324         <clayref idref="SaintThomas"/>
 325         <db:para>Five layers.</db:para>
 326     </sample>
 327     <sample date="2007-12-15" xml:id="T84">
 328         <brushon idref="WhiteBO"/>
 329         <brushon idref="LichenGreenBO"/>
 330         <brushon idref="BlackBO"/>
 331         <clayref idref="SaintThomas"/>
 332         <db:para>The first layer has three vertical stripes which from left to right are white, black and green. The second layer has three horizontal stripes which from top to bottom are white, black, and green. All was done with tape masking, and each stripe had two even coats. This gives a range of a combinations. For instance, in the top right corner one finds white on top of green, and in the left bottom corner green on top of white.</db:para>
 333         <db:para>The black leaked into the white in the first layer and white leaked onto black at the top on the second layer. There was another leakage, not noted down, as well. Basically, the tape for flexible curves couldn't hold it out.</db:para>
 334     </sample>
 335     <sample date="2007-12-15" xml:id="T100">
 336         <brushon idref="BlackBO"/>
 337         <clayref idref="SaintThomas"/>
 338         <db:para>Four layers. The number in the top right corner is drawn over with black AXNER underglaze, and the back says 100. Oops.</db:para>
 339     </sample>
 340     <sample date="2007-12-15" xml:id="T96">
 341         <brushon idref="LichenGreenBO"/>
 342         <clayref idref="SaintThomas"/>
 343         <db:para>Four layers.</db:para>
 344     </sample>
 345     <sample date="2007-12-15" xml:id="T90">
 346         <brushon idref="WhiteBO"/>
 347         <clayref idref="SaintThomas"/>
 348         <db:para>Four layers.</db:para>
 349     </sample>
 350     <sample date="2007-12-15" xml:id="T95">
 351         <brushon idref="OrangeBO"/>
 352         <clayref idref="SaintThomas"/>
 353         <db:para>Five layers, I think. This brush-on acts quite thin.</db:para>
 354     </sample>
 355     <sample date="2007-12-16" xml:id="T88">
 356         <glazing sieved="no" hydrometerGravity="45" idref="FrostedJade"/>
 357         <brushon idref="LichenGreenBO"/>
 358         <clayref idref="SaintThomas"/>
 359         <db:para>The left corner has Lichen Green brushed on top in one thorough layer. In the middle there was a drop of water which gave a visible texture, maybe it shows up after firing. On the right was sprayed, which flooded in a bit under the tape, a fixativ. It prevents the surface from being powderish, but doesn't repell water, athough slows down suction a bit. Not that that is of any use. However, it makes handling a glazed piece with ones hands less destructive. Assuming it doesn't have an effect on after glaze burn. The fixativ was Winsor &amp; Newton Artists' Fixativ, transparent, non removable.</db:para>
 360         <db:para>The frosted jade was one long even dip.</db:para>
 361         <db:para>
 362             <db:date>2007-12-21</db:date> So the Lichen Green area turned into as graphite, and no sign at all from the fixativ. Top right corner is cool, the one below a bit too.</db:para>
 363     </sample>
 364     <sample date="2007-12-15" xml:id="T81">
 365         <brushon idref="JetBlack"/>
 366         <glazing sieved="no" hydrometerGravity="38" idref="Transparent"/>
 367         <clayref idref="SaintThomas"/>
 368         <db:para/>
 369     </sample>
 370     <sample date="2007-12-17" xml:id="T87">
 371         <brushon idref="OrangeBO"/>
 372         <brushon idref="YellowBO"/>
 373         <clayref idref="SaintThomas"/>
 374         <db:para>First, three layers of orange was applied with the usual stair case approach. That is, at the top one layer, and at the bottom three layers. On top of that was three layers of yellow coated over the whole. That is, at the top one finds one layer of orange and and three layers of yellow, and at the bottom three layers of orange and three layers of yellow.</db:para>
 375     </sample>
 376     <sample date="2007-12-17" xml:id="T83">
 377         <brushon idref="RedBO"/>
 378         <brushon idref="YellowBO"/>
 379         <clayref idref="SaintThomas"/>
 380         <db:para>First, three layers of red was applied with the usual stair case approach. That is, at the top one layer, and at the bottom three layers. On top of that was three layers of yellow coated over the whole. That is, at the top one finds one layer of red and and three layers of yellow, and at the bottom three layers of red and three layers of yellow.</db:para>
 381         <db:para>
 382             <db:date>2007-12-21</db:date> Hilarious. Blue and green. I have to have mixed something up.</db:para>
 383     </sample>
 384     <sample date="2007-12-15" xml:id="T97">
 385         <brushon idref="AmacoBrown"/>
 386         <glazing sieved="no" hydrometerGravity="41" idref="Transparent"/>
 387         <clayref idref="SaintThomas"/>
 388         <db:para>Four layers</db:para>
 389     </sample>
 390     <sample date="2007-12-15" xml:id="T94">
 391         <brushon idref="TransparentBO"/>
 392         <brushon idref="JetBlack"/>
 393         <clayref idref="SaintThomas"/>
 394         <db:para>Three layers of black.</db:para>
 395     </sample>
 396     <sample date="2007-12-15" xml:id="T86">
 397         <brushon idref="YellowOatMetal"/>
 398         <glazing sieved="no" hydrometerGravity="41" idref="Transparent"/>
 399         <clayref idref="SaintThomas"/>
 400         <db:para>Four layers.</db:para>
 401     </sample>
 402     <sample date="2007-12-15" xml:id="T71">
 403         <brushon idref="JetBlack"/>
 404         <glazing sieved="no" hydrometerGravity="41" idref="Transparent"/>
 405         <clayref idref="SaintThomas"/>
 406         <db:para>Four layers. It was hard to get a thick layer of transparent glaze on top even though the piece was a bit warm. The black prevented suction.</db:para>
 407     </sample>
 408     <sample date="2007-12-20" xml:id="T82">
 409         <brushon idref="TexturedTan"/>
 410         <clayref idref="SaintThomas"/>
 411         <db:para/>
 412     </sample>
 413     <sample date="2007-12-20" xml:id="T89">
 414         <brushon idref="AmacoYellow"/>
 415         <clayref idref="SaintThomas"/>
 416         <db:para/>
 417     </sample>
 418     <sample date="2007-12-20" xml:id="T85">
 419         <brushon idref="AmacoWhiteUnderglaze"/>
 420         <brushon idref="LichenGreenBO"/>
 421         <brushon idref="JetBlack"/>
 422         <clayref idref="SaintThomas"/>
 423         <db:para>At the bottom, vertically, from left to right: white, black and green. On top, horizontally, from top to bottom: white, black and green. Each strip had two layers, so in total there's four layers on each square.</db:para>
 424     </sample>
 425     <sample date="2007-12-29" xml:id="T93">
 426         <brushon idref="RedBO"/>
 427         <brushon idref="JetBlack"/>
 428         <clayref idref="SaintThomas"/>
 429         <db:para>Five solid layers. Should be fired standing vertically, for testing viscosity.</db:para>
 430         <db:para>
 431             <db:date>2008-01-03</db:date> Loaded it standing more than vertically: maybe 15 degrees "forward."</db:para>
 432         <db:para>Obviously the bottle have been incorrectly labeled. This is not the red spot iron glaze, this is a glossy dark blue. Whatever it is, it didn't run.</db:para>
 433     </sample>
 434     <sample date="2008-01-20" xml:id="T91">
 435         <glazing sieved="no" hydrometerGravity="45" idref="RawBaseLeach"/>
 436         <clayref idref="SaintThomas"/>
 437         <db:para>Slight pink shade(before fired at least) due to the Flint. Very large particles, very powderish. Saturated it with fixativ for that reason. Don't think the third layer is any thicker, due to that it solved away the underlying layers, because of them being too moist. From a <db:constant>200</db:constant>g test batch. </db:para>
 438         <db:para>Looks like porridge. Hilarious, the glaze is for Cone 10, about 1300 C, so the glaze probably didn't melt.</db:para>
 439     </sample>
 440     <sample date="2008-01-28" xml:id="T105">
 441         <glazing sieved="60" hydrometerGravity="46" idref="RawBaseLeach"/>
 442         <clayref idref="SaintThomas"/>
 443         <db:para>Hence, the only difference to <db:xref xlink:href="#T91"/> is that this one was sieved. Used mixer first, and the substance ran through the sieve as water. Beyond the mixing, another reason to it being vastly different could be that it had been mixed in water for a couple of days, and hence dissolved better.</db:para>
 444     </sample>
 445     <sample date="2008-01-28" xml:id="T108">
 446         <glazing sieved="60" hydrometerGravity="49" idref="WhiteLeach"/>
 447         <clayref idref="SaintThomas"/>
 448         <db:para>Leach base with zirconium oxide added.</db:para>
 449     </sample>
 450     <sample date="2008-02-16" xml:id="T107">
 451         <glazing sieved="60" hydrometerGravity="52" idref="WhiterLeach"/>
 452         <clayref idref="SaintThomas"/>
 453         <db:para>Leach base with zirconium oxide added but twice as much as <db:xref xlink:href="#T105"/>. Think it has a small contamination of Candace Black.</db:para>
 454         <db:para>
 455             <db:date>2008-03-09</db:date> Crawling/contractions. Can't be the Zirconium Oxide, since John Britt writes it "has a low expansion and contraction rate." The mixture is completely wrong, it seem to be missing glass body(too little silica, too much alumina), but that doesn't explain why <db:xref xlink:href="#T108"/> looks ok. I suspect documentation error, that I haven't used Alumina for Silica in the case of T108, maybe.</db:para>
 456     </sample>
 457     <sample date="2008-02-16" xml:id="T102">
 458         <glazing sieved="60" hydrometerGravity="52" idref="BlueWhiterLeach"/>
 459         <clayref idref="SaintThomas"/>
 460         <db:para>The shrinking is not caused by the Cobolt oxide, since it's also present in <db:xref xlink:href="#T107"/>.</db:para>
 461     </sample>
 462     <sample date="2008-02-16" xml:id="T104">
 463         <glazing sieved="no" hydrometerGravity="40" idref="Transparent"/>
 464         <clayref idref="SaintThomas"/>
 465         <db:para>Wrote with oxide pen, HC Hobbyceram Sottosmalto NERO 606.</db:para>
 466     </sample>
 467     <sample date="2008-02-16" xml:id="T103">
 468         <glazing sieved="60" hydrometerGravity="52" idref="CandaceBlack"/>
 469         <clayref idref="SaintThomas"/>
 470         <db:para>Used considering a long time, from a <db:constant>200</db:constant> g batch. After the second step, heated with hot air gun. It is so powderish that one layer flaked off. Needs bentonite/CMC for production. Seems the cobolt dispersed unevenly, small black spots at the tops. Sealed of with fixativ. <db:constant>100</db:constant>ml weighted <db:constant>178</db:constant>g.</db:para>
 471     </sample>
 472     <sample date="2008-02-16" xml:id="T106">
 473         <glazing sieved="WithMixer" hydrometerGravity="40" idref="ModifiedTransparentGreen"/>
 474         <clayref idref="SaintThomas"/>
 475         <db:para>From a <db:constant>200</db:constant> g batch. Despite only having a gravity of 40, it was extremely thick. The hydrometer moved slowly and the layers were perceived as very thick.</db:para>
 476         <db:para>
 477             <db:date>2008-02-23</db:date> It's sort of obvious why this turned out as it did. Zinc oxide is a flux, since it's absent the thing didn't melt, and since Tin Oxide is an opacifier, it isn't transparent. I wonder what caused the graphite-look which can be seen on the second and third layer, and a little bit on the first.</db:para>
 478         <db:para>
 479             <db:date>2008-03-09</db:date> Crawling. Could possibly caused by be the Tin oxide, since it has a high contaction rate. Yes, John Britt writes: ""Pinhols, matte surfaces, and rawling sometimes result due to its high viscosity and surface tension, [...]". So that also explains why it's matte. Probably also completely oversaturated with something, considering the graphite-like blackness.</db:para>
 480     </sample>
 481     <sample date="2008-02-16" xml:id="T111">
 482         <glazing sieved="60" hydrometerGravity="51" idref="WillsOribeAlumina"/>
 483         <clayref idref="SaintThomas"/>
 484         <db:para>The middle layer had a lot less Copper on its surface, for some reason. Hm, that's because the copper settles quickly, quicker than the others. Bentonite needed.</db:para>
 485     </sample>
 486     <sample date="2008-02-16" xml:id="T109">
 487         <glazing sieved="60" hydrometerGravity="47" idref="ModifiedMamo"/>
 488         <clayref idref="SaintThomas"/>
 489         <db:para>Right after mixing, so lots of air bubbles. From 200 g batch.</db:para>
 490         <db:para>
 491             <db:date>2008-03-09</db:date> Alumina is very effective, doesn't require much to fuck things up. <db:xref xlink:href="#T110"/> is ok. <db:xref xlink:href="#T137"/> also have issues caused by Alumina, it seems.</db:para>
 492     </sample>
 493     <sample date="2008-02-16" xml:id="T101">
 494         <glazing sieved="60" hydrometerGravity="54" idref="BlueModifiedMamo"/>
 495         <clayref idref="SaintThomas"/>
 496         <db:para>Right after mixing, so lots of air bubbles. From 200 g batch.</db:para>
 497         <db:para>
 498             <db:date>2008-03-09</db:date> See <db:xref xlink:href="#T109"/>.</db:para>
 499     </sample>
 500     <sample date="2008-02-24" xml:id="T112">
 501         <brushon idref="AmacoRedMatt"/>
 502         <clayref idref="SaintThomas"/>
 503         <db:para>Four layers.</db:para>
 504     </sample>
 505     <sample date="2008-02-24" xml:id="T110">
 506         <glazing sieved="WithMixer" hydrometerGravity="42" idref="ModifiedMamoRightAlumina"/>
 507         <clayref idref="SaintThomas"/>
 508         <db:para>From a <db:constant>200</db:constant>g batch.</db:para>
 509     </sample>
 510     <sample date="2008-02-24" xml:id="T152">
 511         <glazing sieved="60" hydrometerGravity="45" idref="CandaceBlack"/>
 512         <clayref idref="SaintThomas"/>
 513         <db:para>Three long dips, 5-6 secs, across whole in order to get a really large thick layer. A noticable increase in weight.</db:para>
 514     </sample>
 515     <sample date="2008-02-28" xml:id="T156">
 516         <glazing sieved="60" hydrometerGravity="55" idref="TitanedHardingOxblood"/>
 517         <clayref idref="SaintThomas"/>
 518         <db:para>From 200g batch. The weight of the 1-2 parts components probably has a usual error margin of one to two grams.</db:para>
 519         <db:para>
 520             <db:date>2008-03-08</db:date> Well, that's how oxblood looks in oxidation, as opposed to reduction. Completely transparent.</db:para>
 521     </sample>
 522     <sample date="2008-02-28" xml:id="T144">
 523         <glazing sieved="60" hydrometerGravity="42" idref="TitanedHardingOxblood"/>
 524         <clayref idref="SaintThomas"/>
 525         <db:para>From 200g batch. The weight of the 1-2 parts components probably has a usual error margin of one to two grams.</db:para>
 526         <db:para>
 527             <db:date>2008-03-08</db:date> Well, that's how oxblood looks in oxidation, as opposed to reduction. Completely transparent.</db:para>
 528     </sample>
 529     <sample date="2008-03-01" xml:id="T130">
 530         <glazing sieved="no" hydrometerGravity="42" idref="Transparent"/>
 531         <clayref idref="SaintThomas"/>
 532         <db:para>To about 10 ml water was about 2 gram Titanium Dioxide(P3362) added, and painted ontop of the glazed, unfired surface(majolica). Flowed very evenly from the brush, compared to for instance Copper Cabonate.</db:para>
 533         <db:para>
 534             <db:date>2008-03-08</db:date> Why yellow? John Britt writes "Titanium dioxide accentuates the color of the clay body and in the presence of iron gives cream colors". Most likely that.</db:para>
 535     </sample>
 536     <sample date="2008-03-01" xml:id="T131">
 537         <glazing sieved="no" hydrometerGravity="42" idref="Transparent"/>
 538         <clayref idref="SaintThomas"/>
 539         <db:para>To about 10 ml water was a "pinch" of Copper Carbonate(P3404), probably 1-3 grams added, and painted ontop of the glazed, unfired surface(majolica).</db:para>
 540     </sample>
 541     <sample date="2008-03-01" xml:id="T140">
 542         <glazing sieved="no" hydrometerGravity="42" idref="Transparent"/>
 543         <clayref idref="SaintThomas"/>
 544         <db:para>The batches used on <db:xref xlink:href="#T136"/> and <db:xref xlink:href="#T131"/> were mixed. So this is Copper Carbonate(P3404) and Zinc Oxide(P3350) mixed.</db:para>
 545         <db:para>
 546             <db:date>2008-03-08</db:date> Interesting to see how quickly the Copper has crept out into the surrounding transparent glaze. Its strong fluxing property at work.</db:para>
 547     </sample>
 548     <sample date="2008-03-01" xml:id="T136">
 549         <glazing sieved="no" hydrometerGravity="42" idref="Transparent"/>
 550         <clayref idref="SaintThomas"/>
 551         <db:para>To about 10 ml water was about 2 g of Zinc Oxide(P3350) added and painted ontop of the glazed, unfired surface(majolica). The volume of oxide was coparatively high, so the layer is thick.</db:para>
 552     </sample>
 553     <sample date="2008-03-01" xml:id="T135">
 554         <glazing sieved="no" hydrometerGravity="42" idref="Transparent"/>
 555         <clayref idref="SaintThomas"/>
 556         <db:para>To about 10 ml water was about 2 gram Tinn Oxide(P3361) added, and painted ontop of the glazed, unfired surface(majolica).</db:para>
 557     </sample>
 558     <sample date="2008-03-01" xml:id="T139">
 559         <glazing sieved="no" hydrometerGravity="42" idref="Transparent"/>
 560         <clayref idref="SaintThomas"/>
 561         <db:para>The batches used on <db:xref xlink:href="#T135"/> and <db:xref xlink:href="#T130"/> were mixed. So this is Tinn Oxide(P3404) and Titanium Dioxide(P3362) mixed.</db:para>
 562         <db:para>
 563             <db:date>2008-03-08</db:date> Why the strong contractions? Tin oxide has a high expansion and contraction which could be why, but that doesn't explain why it's less on <db:xref xlink:href="#T135"/>. These two dudes are fiddling with something together, or is it simply due to an increased amount of these toxides?</db:para>
 564     </sample>
 565     <sample date="2008-03-01" xml:id="T154">
 566         <glazing sieved="no" hydrometerGravity="42" idref="Transparent"/>
 567         <clayref idref="SaintThomas"/>
 568         <db:para>The batches used on <db:xref xlink:href="#T139"/> and <db:xref xlink:href="#T140"/> were mixed. So this is Tinn Oxide(P3404), Titanium Dioxide(P3362), Copper Carbonate(P3404) and Zinc Oxide(P3350).</db:para>
 569     </sample>
 570     <sample date="2008-03-01" xml:id="T141">
 571         <glazing sieved="no" hydrometerGravity="42" idref="Transparent"/>
 572         <clayref idref="SaintThomas"/>
 573         <db:para>To about 10 ml water was about 2 gram Synthetic Red Iron Oxide(P3441) added, and painted ontop of the glazed, unfired surface(majolica).</db:para>
 574     </sample>
 575     <sample date="2008-03-01" xml:id="T151">
 576         <glazing sieved="no" hydrometerGravity="42" idref="Transparent"/>
 577         <clayref idref="SaintThomas"/>
 578         <db:para>To about 10 ml water was about 3 gram Crome Oxide(P3401) added, and painted ontop of the glazed, unfired surface(majolica).</db:para>
 579     </sample>
 580     <sample date="2008-03-01" xml:id="T138">
 581         <glazing sieved="no" hydrometerGravity="42" idref="Transparent"/>
 582         <clayref idref="SaintThomas"/>
 583         <db:para>The batches used on <db:xref xlink:href="#T151"/> and <db:xref xlink:href="#T141"/> were mixed. So this is Synthetic Red Iron Oxide(P3441) and Crome Oxide(P3401).</db:para>
 584         <db:para>
 585             <db:date>2008-03-08</db:date> I can swear that the surrounding transparent is tinted towards green. Crome is a super strong colorant, but did it really manage to walk over there? Can't find anything supporting that chrome should have strong fluxing properties but considering that it is coloring rather evenly, that might be the case.</db:para>
 586     </sample>
 587     <sample date="2008-03-01" xml:id="T133">
 588         <glazing sieved="no" hydrometerGravity="42" idref="Transparent"/>
 589         <clayref idref="SaintThomas"/>
 590         <db:para>The batches used on <db:xref xlink:href="#T138"/> and <db:xref xlink:href="#T154"/> were mixed. So this is Synthetic Red Iron Oxide(P3441), Crome Oxide(P3401), Tinn Oxide(P3404), Titanium Dioxide(P3362), Copper Carbonate(P3404) and Zinc Oxide(P3350).</db:para>
 591         <db:para>
 592             <db:date>2008-03-08</db:date> Interesting to see how quickly the Copper has crept out into the surrounding transparent glaze. Its strong fluxing property at work.</db:para>
 593     </sample>
 594     <sample date="2008-03-01" xml:id="T132">
 595         <glazing sieved="no" hydrometerGravity="42" idref="Transparent"/>
 596         <clayref idref="SaintThomas"/>
 597         <db:para>To about 10 ml water was about 2 gram Black Iron Oxide(P3408) added, and painted ontop of the glazed, unfired surface(majolica). Large particles, dispersing unevenly with the brush.</db:para>
 598     </sample>
 599     <sample date="2008-03-01" xml:id="T157">
 600         <glazing sieved="no" hydrometerGravity="42" idref="Transparent"/>
 601         <clayref idref="SaintThomas"/>
 602         <db:para>To about 10 ml water was about 2 gram Cobalt Carbonate(P3402) added, and painted ontop of the glazed, unfired surface(majolica).</db:para>
 603     </sample>
 604     <sample date="2008-03-01" xml:id="T155">
 605         <glazing sieved="no" hydrometerGravity="42" idref="Transparent"/>
 606         <clayref idref="SaintThomas"/>
 607         <db:para>The batches used on <db:xref xlink:href="#T132"/> and <db:xref xlink:href="#T157"/> were mixed. So this is Black Iron Oxide(P3408) and Cobalt Carbonate(P3402).</db:para>
 608     </sample>
 609     <sample date="2008-03-01" xml:id="T134">
 610         <glazing sieved="no" hydrometerGravity="42" idref="Transparent"/>
 611         <clayref idref="SaintThomas"/>
 612         <db:para>To about 10 ml water was about 2 gram Cobalt Oxide(P3403) added, and painted ontop of the glazed, unfired surface(majolica).</db:para>
 613     </sample>
 614     <sample date="2008-03-01" xml:id="T147">
 615         <glazing sieved="no" hydrometerGravity="42" idref="Transparent"/>
 616         <clayref idref="SaintThomas"/>
 617         <db:para>To about 10 ml water was about 2 gram Magnesium Carbonate(P3331) added, and painted ontop of the glazed, unfired surface(majolica).</db:para>
 618         <db:para>
 619             <db:date>2008-03-09</db:date> A nice demonstration to why there exists such a thing as "Magnesium Matte Glazes."</db:para>
 620     </sample>
 621     <sample date="2008-03-01" xml:id="T137">
 622         <glazing sieved="no" hydrometerGravity="60" idref="TransparentGreen"/>
 623         <clayref idref="SaintThomas"/>
 624         <db:para>Very high gravity, didn't get a stable reading, somewhere about 60-70.</db:para>
 625         <db:para>
 626             <db:date>2008-03-08</db:date> The glaze is documented for oxidation, so how come it's speckled and opaque? Can the excessive alumina be really be blamed? Yes, seems so, John Britt: "The presence of alumina in a glaze inhibits color response and produces dull colors and matte surfaces."</db:para>
 627     </sample>
 628     <sample date="2008-03-01" xml:id="T148">
 629         <glazing sieved="no" hydrometerGravity="40" idref="TransparentGreen"/>
 630         <clayref idref="SaintThomas"/>
 631         <db:para>
 632             <db:date>2008-03-08</db:date> See T137</db:para>
 633     </sample>
 634     <sample date="2008-03-01" xml:id="T143">
 635         <glazing sieved="no" hydrometerGravity="42" idref="HardingOxblood"/>
 636         <clayref idref="SaintThomas"/>
 637         <db:para/>
 638     </sample>
 639     <sample date="2008-03-01" xml:id="T150">
 640         <glazing sieved="no" hydrometerGravity="53" idref="PerfectBlack"/>
 641         <clayref idref="SaintThomas"/>
 642         <db:para/>
 643     </sample>
 644     <sample date="2008-03-01" xml:id="T149">
 645         <glazing sieved="no" hydrometerGravity="42" idref="PerfectBlack"/>
 646         <clayref idref="SaintThomas"/>
 647         <db:para>Feels like this one can be much thinner but still work.</db:para>
 648     </sample>
 649     <sample date="2008-03-08" xml:id="T166">
 650         <brushon idref="TivoliRed"/>
 651         <clayref idref="SaintThomas"/>
 652         <db:para/>
 653     </sample>
 654     <sample date="2008-03-08" xml:id="T199">
 655         <brushon idref="TivoliRed"/>
 656         <clayref idref="WSW"/>
 657         <db:para/>
 658     </sample>
 659     <sample date="2008-03-08" xml:id="T153">
 660         <brushon idref="AutumnShades"/>
 661         <clayref idref="WSW"/>
 662         <db:para/>
 663     </sample>
 664     <sample date="2008-03-08" xml:id="T201">
 665         <brushon idref="AutumnShades"/>
 666         <clayref idref="SaintThomas"/>
 667         <db:para/>
 668     </sample>
 669     <sample date="2008-03-08" xml:id="T145">
 670         <brushon idref="CrystalBlue"/>
 671         <clayref idref="SaintThomas"/>
 672         <db:para/>
 673     </sample>
 674     <sample date="2008-03-08" xml:id="T189">
 675         <brushon idref="CrystalBlue"/>
 676         <clayref idref="WSW"/>
 677         <db:para/>
 678     </sample>
 679     <sample date="2008-03-08" xml:id="T187">
 680         <brushon idref="AmacoClear"/>
 681         <clayref idref="WSW"/>
 682         <db:para/>
 683     </sample>
 684     <sample date="2008-03-08" xml:id="T146">
 685         <brushon idref="AmacoClear"/>
 686         <clayref idref="SaintThomas"/>
 687         <db:para/>
 688     </sample>
 689     <sample date="2008-03-08" xml:id="T162">
 690         <brushon idref="AmacoHazyPink"/>
 691         <clayref idref="SaintThomas"/>
 692         <db:para/>
 693     </sample>
 694     <sample date="2008-03-08" xml:id="T192">
 695         <brushon idref="AmacoHazyPink"/>
 696         <clayref idref="WSW"/>
 697         <db:para/>
 698     </sample>
 699     <sample date="2008-03-08" xml:id="T171">
 700         <brushon idref="AmacoLavender"/>
 701         <clayref idref="SaintThomas"/>
 702         <db:para/>
 703     </sample>
 704     <sample date="2008-03-08" xml:id="T196">
 705         <brushon idref="AmacoLavender"/>
 706         <clayref idref="WSW"/>
 707         <db:para/>
 708     </sample>
 709     <sample date="2008-03-08" xml:id="T161">
 710         <glazing sieved="no" hydrometerGravity="49" idref="ModifiedMamoRightAlumina"/>
 711         <glazing sieved="no" hydrometerGravity="42" idref="Transparent"/>
 712         <clayref idref="SaintThomas"/>
 713         <db:para>Batch has been standing for a week or so, shaked it thoroughly. Fucked up the right bottom corner by touching with a finger while it was wet.</db:para>
 714     </sample>
 715     <sample date="2008-03-08" xml:id="T181">
 716         <glazing sieved="no" hydrometerGravity="49" idref="ModifiedMamoRightAlumina"/>
 717         <glazing sieved="no" hydrometerGravity="42" idref="Transparent"/>
 718         <clayref idref="WSW"/>
 719         <db:para>Batch has been standing for a week or so, shaked it thoroughly.</db:para>
 720     </sample>
 721     <sample date="2008-03-09" xml:id="T169">
 722         <glazing sieved="WithMixer" hydrometerGravity="46" idref="HamadaBase"/>
 723         <clayref idref="SaintThomas"/>
 724         <db:para>From 200 g batch.</db:para>
 725     </sample>
 726     <sample date="2008-03-09" xml:id="T180">
 727         <glazing sieved="WithMixer" hydrometerGravity="46" idref="HamadaBase"/>
 728         <clayref idref="WSW"/>
 729         <db:para>From 200 g batch.</db:para>
 730     </sample>
 731     <sample date="2008-03-09" xml:id="T186">
 732         <glazing sieved="WithMixer" hydrometerGravity="50" idref="HamadaBase5Talc"/>
 733         <clayref idref="WSW"/>
 734         <db:para>From 200 g batch.</db:para>
 735     </sample>
 736     <sample date="2008-03-09" xml:id="T167">
 737         <glazing sieved="WithMixer" hydrometerGravity="50" idref="HamadaBase5Talc"/>
 738         <clayref idref="SaintThomas"/>
 739         <db:para>From 200 g batch.</db:para>
 740     </sample>
 741     <sample date="2008-03-09" xml:id="T183">
 742         <glazing sieved="WithMixer" hydrometerGravity="53" idref="HamadaBase20Talc"/>
 743         <clayref idref="WSW"/>
 744         <db:para>From 200 g batch. To the 5 parts batch, which was already extended from 0% talc, was added 15 parts talc. Since four tiles have already been dipped, the amount of talc is probably a bit higher than 20.</db:para>
 745     </sample>
 746     <sample date="2008-03-09" xml:id="T163">
 747         <glazing sieved="WithMixer" hydrometerGravity="53" idref="HamadaBase20Talc"/>
 748         <clayref idref="SaintThomas"/>
 749         <db:para>From 200 g batch. To the 5 parts batch, which was already extended from 0% talc, was added 15 parts talc. Since four tiles have already been dipped, the amount of talc is probably a bit higher than 20.</db:para>
 750     </sample>
 751     <sample date="2008-03-09" xml:id="T170">
 752         <glazing sieved="WithMixer" hydrometerGravity="39" idref="ChromeTransparentGreen"/>
 753         <clayref idref="SaintThomas"/>
 754         <db:para>From 200 g batch.</db:para>
 755     </sample>
 756     <sample date="2008-03-09" xml:id="T185">
 757         <glazing sieved="WithMixer" hydrometerGravity="39" idref="ChromeTransparentGreen"/>
 758         <clayref idref="WSW"/>
 759         <db:para>From 200g batch. By mistake I brushed away a bit from the left bottom corner. Might well be that it will look like an expansion problem.</db:para>
 760     </sample>
 761     <sample date="2008-03-09" xml:id="T175">
 762         <clayref idref="SaintThomas"/>
 763         <db:para>Melt test of P3110, Ferro frit</db:para>
 764     </sample>
 765     <sample date="2008-03-09" xml:id="T173">
 766         <clayref idref="SaintThomas"/>
 767         <db:para>Melt test of P3316, Feldspar FFF</db:para>
 768     </sample>
 769     <sample date="2008-03-09" xml:id="T177">
 770         <clayref idref="SaintThomas"/>
 771         <db:para>Melt test of P3342, Soda Ash</db:para>
 772     </sample>
 773     <sample date="2008-03-09" xml:id="T178">
 774         <clayref idref="SaintThomas"/>
 775         <db:para>Melt test of P3134, High Alcaline Ferro Frit</db:para>
 776     </sample>
 777     <sample date="2008-03-09" xml:id="T176">
 778         <clayref idref="SaintThomas"/>
 779         <db:para>Melt test of P3309, China Clay</db:para>
 780     </sample>
 781     <sample date="2008-03-09" xml:id="T172">
 782         <clayref idref="SaintThomas"/>
 783         <db:para>Melt test of P3317, Feldspar Soda</db:para>
 784     </sample>
 785     <sample date="2008-03-09" xml:id="T174">
 786         <clayref idref="SaintThomas"/>
 787         <db:para>Melt test of P3315, Dolomite</db:para>
 788     </sample>
 789     <sample date="2008-03-17" xml:id="T191">
 790         <glazing sieved="no" hydrometerGravity="39" idref="Transparent"/>
 791         <clayref idref="WSW"/>
 792         <db:para>A pinch of Manganese Oxide(from Alt For Keramikk) was mixed with water and painted on top of the transparent.</db:para>
 793     </sample>
 794     <sample date="2008-03-19" xml:id="T237">
 795         <glazing sieved="no" hydrometerGravity="44" idref="Transparent"/>
 796         <clayref idref="WSW"/>
 797         <db:para>The right side has a slip consisting of "Puraflo", UK Origin, WBB Minerals. Probably pipleire. The clay is spot-wise contaminated with Saint Thomas. Might be that the id is T231.</db:para>
 798     </sample>
 799     <sample date="2008-03-19" xml:id="T235">
 800         <glazing sieved="no" hydrometerGravity="44" idref="Transparent"/>
 801         <clayref idref="SaintThomas"/>
 802         <db:para>The right side has a slip consisting of "Puraflo", UK Origin, WBB Minerals. Probably pipleire.</db:para>
 803     </sample>
 804     <sample date="2008-03-01" xml:id="T209">
 805         <glazing sieved="no" hydrometerGravity="39" idref="Transparent"/>
 806         <clayref idref="SaintThomas"/>
 807         <db:para>To about 10 ml water was about 2 gram Rutile(from Alt For Keramikk) added, and painted ontop of the glazed, unfired surface(majolica).</db:para>
 808     </sample>
 809     <sample date="2008-03-20" xml:id="T165">
 810         <glazing sieved="no" hydrometerGravity="47" idref="ClausCrystalGreenBlack"/>
 811         <clayref idref="SaintThomas"/>
 812         <db:para>From 200g batch.</db:para>
 813     </sample>
 814     <sample date="2008-03-29" xml:id="T218">
 815         <glazing sieved="no" hydrometerGravity="39" idref="ClausCrystalGreenBlack"/>
 816         <clayref idref="SaintThomas"/>
 817         <db:para>From 200g batch. Three second dips.</db:para>
 818     </sample>
 819     <sample date="2008-03-20" xml:id="T204">
 820         <glazing sieved="no" hydrometerGravity="33" idref="ClausCrystalGreenBlack"/>
 821         <clayref idref="SaintThomas"/>
 822         <db:para>From 200g batch. The gravity is estimated. This hydrometer goes to 40, and it sunk to... about 33?</db:para>
 823     </sample>
 824     <sample date="2008-03-20" xml:id="T220">
 825         <glazing sieved="no" hydrometerGravity="39" idref="Transparent"/>
 826         <clayref idref="SaintThomas"/>
 827         <db:para>To about 10 ml water was about 2 gram yellow stain(P4140) mixed and painted ontop of the glazed, unfired surface(majolica).</db:para>
 828     </sample>
 829     <sample date="2008-03-20" xml:id="T213">
 830         <glazing sieved="no" hydrometerGravity="39" idref="ModifiedMamoRightAlumina"/>
 831         <clayref idref="SaintThomas"/>
 832         <db:para>To about 10 ml water was about 2 gram yellow stain(P4140) mixed and painted ontop of the glazed, unfired surface(majolica).</db:para>
 833     </sample>
 834     <sample date="2008-03-20" xml:id="T203">
 835         <glazing sieved="no" hydrometerGravity="51" idref="WhiteGloss"/>
 836         <clayref idref="SaintThomas"/>
 837         <db:para>To about 10 ml water was about 2 gram yellow stain(P4140) mixed and painted ontop of the glazed, unfired surface(majolica).</db:para>
 838         <db:para>The id has been corrected, clarified on the back side.</db:para>
 839     </sample>
 840     <sample date="2008-03-20" xml:id="T219">
 841         <clayref idref="SaintThomas"/>
 842         <db:para>Melt test of Bone Ash, P3305. An arbitrary amount.</db:para>
 843         <db:para>A small, round, white detached stone.</db:para>
 844     </sample>
 845     <sample date="2008-03-20" xml:id="T202">
 846         <clayref idref="SaintThomas"/>
 847         <db:para>Melt test of Whiting, P3346. An arbitrary amount.</db:para>
 848         <db:para>Nothing melted, fully powderish and most of it fell out.</db:para>
 849     </sample>
 850     <sample date="2008-03-20" xml:id="T222">
 851         <clayref idref="SaintThomas"/>
 852         <db:para>Melt test of Talcum, P3345. An arbitrary amount.</db:para>
 853         <db:para>Evidently, didn't melt at all.</db:para>
 854     </sample>
 855     <sample date="2008-03-20" xml:id="T217">
 856         <glazing sieved="WithMixer" hydrometerGravity="41" idref="SatinBase"/>
 857         <clayref idref="SaintThomas"/>
 858         <db:para>From 200 g batch.</db:para>
 859     </sample>
 860     <sample date="2008-03-20" xml:id="T214">
 861         <glazing sieved="WithMixer" hydrometerGravity="43" idref="GreenBlueSatin"/>
 862         <clayref idref="SaintThomas"/>
 863         <db:para>From 200 g batch.</db:para>
 864         <db:para>The id looks like 219 but is 214, clarified on the back side.</db:para>
 865     </sample>
 866     <sample date="2008-03-22" xml:id="T207">
 867         <glazing sieved="WithMixer" hydrometerGravity="42" idref="ModifiedSatinWhite"/>
 868         <clayref idref="SaintThomas"/>
 869         <db:para>From 200 g batch.</db:para>
 870     </sample>
 871     <sample date="2008-03-22" xml:id="T160">
 872         <glazing sieved="WithMixer" hydrometerGravity="42" idref="ModifiedSatinWhite"/>
 873         <clayref idref="SaintThomas"/>
 874         <db:para>From 200 g batch.</db:para>
 875         <db:para>To about 10 ml water was about 2 gram yellow stain(P4140) mixed and painted ontop of the glazed, unfired surface(majolica).</db:para>
 876     </sample>
 877     <sample date="2008-03-22" xml:id="T224">
 878         <glazing sieved="WithMixer" hydrometerGravity="44" idref="GreenModifiedSatinWhite"/>
 879         <clayref idref="SaintThomas"/>
 880         <db:para>From 200 g batch.</db:para>
 881     </sample>
 882     <sample date="2008-03-22" xml:id="T221">
 883         <glazing sieved="WithMixer" hydrometerGravity="44" idref="GreenModifiedSatinWhite"/>
 884         <clayref idref="SaintThomas"/>
 885         <db:para>From 200 g batch.</db:para>
 886         <db:para>To about 10 ml water was about 2 gram yellow stain(P4140) mixed and painted ontop of the glazed, unfired surface(majolica).</db:para>
 887         <db:para>
 888             <db:date>2008-03-29</db:date> The yellow stain is powder on the surface, it didn't mix with the glaze.</db:para>
 889     </sample>
 890     <sample date="2008-03-22" xml:id="T211">
 891         <glazing sieved="WithMixer" hydrometerGravity="44" idref="SatinGlossGreenBlack"/>
 892         <clayref idref="SaintThomas"/>
 893         <db:para>From 200 g batch. Very thick and feel heavy.</db:para>
 894     </sample>
 895     <sample date="2008-03-22" xml:id="T164">
 896         <glazing sieved="WithMixer" hydrometerGravity="28" idref="SatinGlossGreenBlack"/>
 897         <clayref idref="SaintThomas"/>
 898         <db:para>From 200 g batch. Hydrometer is completely estimated. It sunk far away from the grading. Could easily be 20 or 32.</db:para>
 899         <db:para>To about 10 ml water was about 2 gram yellow stain(P4140) mixed and painted ontop of the glazed, unfired surface(majolica).</db:para>
 900     </sample>
 901     <sample date="2008-03-23" xml:id="T212">
 902         <clayref idref="SaintThomas"/>
 903         <db:para>Melt test of P3314, Cornish Stone.</db:para>
 904         <db:para>A detached, cornish, gray stone.</db:para>
 905     </sample>
 906     <sample date="2008-04-13" xml:id="T205">
 907         <glazing sieved="WithMixer" hydrometerGravity="45" idref="NewGrassGreen"/>
 908         <clayref idref="SaintThomas"/>
 909         <db:para>Very thick at the bottom, the Bentonite surely is at work.</db:para>
 910         <db:para><db:date>2008-05-19</db:date> So this batch of <db:xref
 911                 xlink:href="#NewGrassGreen"/> went madly wrong: chrome brown
 912             instead of chrome green. What could have been the cause? The keys
 913             is likely in what John Britt writes about Chrome: "In a glaze that
 914             contains tin oxide, the chronium oxide encourages some pink
 915             coloration; in one that contains zinc oxide, adding chronium oxide
 916             will produce browns. In high barium or sodium glazes, less than 1
 917             percent chronium oxide will produce intense <db:phrase
 918                 xlink:href="http://en.wikipedia.org/wiki/Chartreuse_%28color%29">chartreuse</db:phrase>
 919             yellow/green colors. Chrome oxide is unaffected by oxidation and
 920             reduction."(The Complete Guide to High-Fire Glazes, p. 22). Hence,
 921             relevant questions are: was barium carbonate forgotten? Was Zinc
 922             confused with Tin? Is Nepheline Syenite a Custer Feldspar? What
 923             provides sodium?</db:para>
 924     </sample>
 925     <sample date="2008-04-13" xml:id="T215">
 926         <glazing sieved="WithMixer" hydrometerGravity="45" idref="NewGrassGreen"/>
 927         <clayref idref="SaintThomas"/>
 928         <db:para>Only one dip.</db:para>
 929     </sample>
 930     <sample date="2008-04-13" xml:id="T198">
 931         <glazing sieved="WithMixer" hydrometerGravity="45" idref="NewGrassGreen"/>
 932         <clayref idref="WSW"/>
 933         <db:para>Only one dip.</db:para>
 934     </sample>
 935     <sample date="2008-04-13" xml:id="T206">
 936         <glazing sieved="WithMixer" hydrometerGravity="32" idref="NewGrassGreen"/>
 937         <clayref idref="SaintThomas"/>
 938         <db:para>The gravity number is estimated. Somewhere below 40, that's for sure. Fairly thin.</db:para>
 939         <db:para>It melted, but the color is wrong.</db:para>
 940
 941     </sample>
 942     <sample date="2008-04-13" xml:id="T248">
 943         <glazing sieved="WithMixer" hydrometerGravity="57" idref="SatinBase"/>
 944         <clayref idref="SaintThomas"/>
 945         <db:para>Perceived as very thick. Didn't make it into the two bottom holes. From 2000 g batch.</db:para>
 946     </sample>
 947     <sample date="2008-04-13" xml:id="T225">
 948         <glazing sieved="WithMixer" hydrometerGravity="50" idref="SatinBase"/>
 949         <clayref idref="SaintThomas"/>
 950         <db:para>Perceived as very thick. From 2000 g batch.</db:para>
 951     </sample>
 952     <sample date="2008-04-13" xml:id="T242">
 953         <glazing sieved="WithMixer" hydrometerGravity="42" idref="SatinBase5Zirconium"/>
 954         <clayref idref="SaintThomas"/>
 955         <db:para>From 2000 g batch.</db:para>
 956     </sample>
 957     <sample date="2008-04-13" xml:id="T246">
 958         <glazing sieved="WithMixer" hydrometerGravity="47" idref="WillsOribeAlumina"/>
 959         <clayref idref="SaintThomas"/>
 960         <db:para>From 200 g batch.</db:para>
 961     </sample>
 962     <sample date="2008-04-13" xml:id="T234">
 963         <glazing sieved="WithMixer" hydrometerGravity="50" idref="BlueFire"/>
 964         <clayref idref="SaintThomas"/>
 965         <db:para>From 200 g batch.</db:para>
 966     </sample>
 967     <sample date="2008-04-13" xml:id="T243">
 968         <glazing sieved="WithMixer" hydrometerGravity="35" idref="BlueFire"/>
 969         <clayref idref="SaintThomas"/>
 970         <db:para>From 200 g batch. Gravity number is estimate. Below 40, that is known.</db:para>
 971     </sample>
 972     <sample date="2008-04-14" xml:id="T228">
 973         <glazing sieved="no" hydrometerGravity="39" idref="Transparent"/>
 974         <clayref idref="SaintThomas"/>
 975         <db:para>To about 10 ml water was about 2 gram Barium Carbonate(P3303) added, painted ontop of the glazed, unfired surface(majolica).</db:para>
 976     </sample>
 977     <sample date="2008-04-14" xml:id="T229">
 978         <glazing sieved="no" hydrometerGravity="39" idref="Transparent"/>
 979         <clayref idref="SaintThomas"/>
 980         <db:para>To about 10 ml water was about 2 gram Lithium Carbonate(R1063) added, painted ontop of the glazed, unfired surface(majolica). The orange(iron?) flashes at the top is strong, also seen on <db:xref xlink:href="#T227"/>, and not seen on anything else in the same kiln firing, so probably the Lithium did that, somehow. The glaze has crazed, but isn't it outside of where the lithium was brushed on?</db:para>
 981     </sample>
 982     <sample date="2008-04-14" xml:id="T227">
 983         <glazing sieved="no" hydrometerGravity="39" idref="Transparent"/>
 984         <clayref idref="SaintThomas"/>
 985         <db:para>The batches used on <db:xref xlink:href="#T229"/> and <db:xref xlink:href="#T228"/> were mixed. So this is Lithium Carbonate(R1063) and Barium Carbonate(P3303) mixed.</db:para>
 986     </sample>
 987     <sample date="2008-04-14" xml:id="T230">
 988         <glazing sieved="WithMixer" hydrometerGravity="42" idref="OpaqueGlossWhite"/>
 989         <clayref idref="SaintThomas"/>
 990         <db:para>The glaze flowed very thickly.</db:para>
 991     </sample>
 992     <sample date="2008-04-14" xml:id="T194">
 993         <glazing sieved="WithMixer" hydrometerGravity="42" idref="OpaqueGlossWhite"/>
 994         <clayref idref="WSW"/>
 995         <db:para>The glaze flowed very thickly.</db:para>
 996     </sample>
 997     <sample date="2008-04-14" xml:id="T193">
 998         <glazing sieved="60" hydrometerGravity="36" idref="OpaqueGlossWhite"/>
 999         <clayref idref="WSW"/>
1000         <db:para>The gravity number is estimated, although fairly well. It's at least below 40. Glazed only one layer.</db:para>
1001     </sample>
1002
1003     <sample date="2008-04-19" xml:id="T216">
1004         <clayref idref="SaintThomas"/>
1005         <db:para>Melt test of P3332, Nepheline Syenite</db:para>
1006     </sample>
1007
1008     <sample date="2008-04-20" xml:id="T249">
1009         <glazing sieved="WithMixer" hydrometerGravity="32" idref="NewGrassGreen"/>
1010         <brushon idref="VelourBlackBO"/>
1011         <clayref idref="SaintThomas"/>
1012         <db:para>The gravity number is estimated. Somewhere below 40, that's for sure. Fairly thin.</db:para>
1013         <db:para>The underglaze dramatically inhibited the suction. The glaze ontop floated around like water, more or less. Possibly one could dillute the underglaze. One idea could also be to spray the underglaze on before bisque firing, both things could improve suction. Though I think all <db:xref xlink:href="#NewGrassGreen"/> will come out as crap, since it's for cone 10.</db:para>
1014
1015     </sample>
1016
1017     <sample date="2008-04-20" xml:id="T233">
1018         <glazing sieved="no" hydrometerGravity="34" idref="GlossBlackBreakingBrown"/>
1019         <clayref idref="SaintThomas"/>
1020         <db:para>The gravity number is estimated. Somewhere below 40, that's for sure. Fairly thin. Mixed it a bit, but the mixer is broken. Settles quickly due to the heavy and large iron oxide particles. Seems to be dispersing unevenly for the same reason. Won't pass a 100 mesh sieve.</db:para>
1021     </sample>
1022
1023     <sample date="2008-04-20" xml:id="T231">
1024         <glazing sieved="100" hydrometerGravity="39" idref="BlankBaseWithNewGrass"/>
1025         <clayref idref="SaintThomas"/>
1026         <db:para>Was fairly clumsy when dipping. There's three layers.</db:para>
1027     </sample>
1028
1029     <sample date="2008-04-20" xml:id="T250">
1030         <glazing sieved="100" hydrometerGravity="39" idref="BlankBaseWithNewGrass"/>
1031         <clayref idref="SaintThomas"/>
1032         <db:para>One layer. Id has been corrected, from 203 to 250.</db:para>
1033     </sample>
1034
1035     <sample date="2008-04-20" xml:id="T190">
1036         <glazing sieved="100" hydrometerGravity="47" idref="BlankBaseWithNewGrass"/>
1037         <clayref idref="WSW"/>
1038         <db:para>One layer. Felt failry thick</db:para>
1039     </sample>
1040
1041     <sample date="2008-04-20" xml:id="T210">
1042         <glazing sieved="100" hydrometerGravity="40" idref="GlossRutiledBlue"/>
1043         <clayref idref="SaintThomas"/>
1044         <db:para></db:para>
1045     </sample>
1046
1047     <sample date="2008-04-20" xml:id="T182">
1048         <glazing sieved="100" hydrometerGravity="40" idref="GlossRutiledBlue"/>
1049         <clayref idref="WSW"/>
1050         <db:para>One layer.</db:para>
1051     </sample>
1052
1053     <sample date="2008-04-20" xml:id="T232">
1054         <glazing sieved="100" hydrometerGravity="43" idref="GlossBlackBreakingBrown"/>
1055         <clayref idref="SaintThomas"/>
1056         <db:para/>
1057     </sample>
1058
1059     <sample date="2008-05-17" xml:id="T200">
1060         <glazing sieved="WithMixer" hydrometerGravity="49" idref="ClausCrystalGreenBlack"/>
1061         <clayref idref="WSW"/>
1062         <db:para>From 2000 g slurry, just mixed. One layer.</db:para>
1063         <db:para><db:date>2008-05-24</db:date> All the pieces with glaze in this firing, <db:xref xlink:href="#T197"/>, <db:xref xlink:href="#P50"/>, <db:xref xlink:href="#P54"/>, has one thing in common: they all have small white elevates dots over them. Looks like accumuations of... calcium? Looks like small melt tests, reminds of <db:xref xlink:href="#T216"/>.</db:para>
1064     </sample>
1065
1066     <sample date="2008-05-17" xml:id="T188">
1067         <glazing sieved="WithMixer" hydrometerGravity="50" idref="WillsOribeAlumina"/>
1068         <clayref idref="WSW"/>
1069         <db:para>From 2000 g slurry, just mixed. One layer.</db:para>
1070     </sample>
1071
1072     <sample date="2008-05-19" xml:id="T197">
1073         <glazing sieved="no" hydrometerGravity="46" idref="ClausCrystalGreenBlack"/>
1074         <clayref idref="WSW"/>
1075         <db:para>From 2000 g slurry, stirred up with spoon. Should be the same
1076             as <db:xref xlink:href="#T200"/> with the difference that the
1077             slurry has been standing for about three days. Wonder why the hydrometer reading was lower, 46 as opposed to 49 a couple of days ago.</db:para>
1078     </sample>
1079
1080     <sample date="2008-05-19" xml:id="T195">
1081         <glazing sieved="no" hydrometerGravity="50" idref="WillsOribeAlumina"/>
1082         <clayref idref="WSW"/>
1083         <db:para>From 2000 g slurry, stirred up with spoon. Should be the same
1084             as <db:xref xlink:href="#T188"/> with the difference that the
1085             slurry has been standing for about three days.</db:para>
1086     </sample>
1087
1088     <sample date="2008-05-19" xml:id="W197">
1089         <glazing sieved="WithMixer" hydrometerGravity="45" idref="NewGrassGreen"/>
1090         <clayref idref="WSW"/>
1091         <db:para>From 200 g slurry, direct after mixing, second batch. </db:para>
1092     </sample>
1093
1094     <sample date="2008-05-19" xml:id="T244">
1095         <glazing sieved="WithMixer" hydrometerGravity="45" idref="NewGrassGreen"/>
1096         <brushon idref="VelourBlackBO"/>
1097         <brushon idref="WhiteBO"/>
1098         <clayref idref="SaintThomas"/>
1099         <db:para>From 200 g slurry, direct after mixing, second batch. Black on the right, white on the left. One layer with green, on top of the other.</db:para>
1100         <db:para><db:date>2008-05-24</db:date> Interestingly the green turns brown when appearing on top of the white, which suggests that the commercial white brush-on contains Zinc. And its Material Safety Data Sheet(cosh438) confirms this, 2.5-24% of ZnO.</db:para>
1101     </sample>
1102
1103     <sample date="2008-05-19" xml:id="T247">
1104         <glazing sieved="WithMixer" hydrometerGravity="45" idref="NewGrassGreen"/>
1105         <clayref idref="SaintThomas"/>
1106         <db:para>From 200 g slurry, direct after mixing, second batch. Three layers. The left bottom corner has a stain from <db:xref xlink:href="#WhiteGloss"/> and some damage from trying to remove it. Which doesn't show at all after firing.</db:para>
1107
1108         <db:para>Seems the reasoning for <db:xref xlink:href="#T205"/> was correct, since these tiles, including <db:xref xlink:href="#T245"/> <db:xref xlink:href="#W184"/>, are green. But still very boring, probably too much Chrome and something's missing to making it speckle.</db:para>
1109     </sample>
1110
1111     <sample date="2008-05-19" xml:id="W179">
1112         <glazing sieved="WithMixer" hydrometerGravity="45" idref="NewGrassGreen"/>
1113         <glazing sieved="WithMixer" hydrometerGravity="49" idref="WhiteGloss"/>
1114         <clayref idref="WSW"/>
1115         <db:para>From 200 g slurry, direct after mixing, second batch. Three layers. White was on top.</db:para>
1116     </sample>
1117
1118     <sample date="2008-05-19" xml:id="T245">
1119         <glazing sieved="WithMixer" hydrometerGravity="40" idref="NewGrassGreen"/>
1120         <clayref idref="SaintThomas"/>
1121         <db:para>From 200 g slurry, direct after mixing, second batch. One layer.</db:para>
1122     </sample>
1123
1124     <sample date="2008-05-19" xml:id="W184">
1125         <glazing sieved="WithMixer" idref="NewGrassGreen"/>
1126         <clayref idref="WSW"/>
1127         <db:para>From 200 g slurry, direct after mixing, second batch. Forgot to write this one down, hydrometer reading unknown, somewhere between 40 and 50.</db:para>
1128     </sample>
1129
1130     <sample date="2008-05-24" xml:id="W429">
1131         <glazing hydrometerGravity="45" sieved="no" idref="ClausCrystalGreenBlack"/>
1132         <glazing hydrometerGravity="41" sieved="no" idref="Transparent"/>
1133         <clayref idref="WSW"/>
1134         <db:para>Green on top of transparent. Fired standing vertically.</db:para>
1135     </sample>
1136
1137     <sample date="2008-05-24" xml:id="W411">
1138         <glazing hydrometerGravity="45" sieved="no" idref="ClausCrystalGreenBlack"/>
1139         <glazing hydrometerGravity="41" sieved="no" idref="Transparent"/>
1140         <clayref idref="WSW"/>
1141         <db:para>Transparent on top of green. Fired standing vertically.</db:para>
1142     </sample>
1143
1144
1145     <!-- TODO 251 Velour black
1146         Intended for newgrassgreen.
1147         <db:para>Id has been corrected. From 224 to 251.</db:para>
1148
1149     -->
1150
1151     <!-- Made samples 101-112. Made samples 130 - 15? , 160-201, 202-222, 223-234, 235-241, 242 - 249, 250-251, 400-450. -->
1152     <!--
1153
1154     Questions:
1155     - What is a /secondary/ flux?
1156     - What does UMF mean?
1157     - Where shall one throw glaze slurries? Paining oxides?
1158     - What's the mesh size on the sieve at liv i leire?
1159     - What is the black stuff on T246?
1160     - Why did 182 come out as it did?
1161     - Why did 234/243 come out as it did?
1162     - How should one lowering the melting point of a glaze? A cone or two. Say NewGrassGreen.
1163     - How should one approach food safety? Should one only use liner glazes? When is a glaze food safe?
1164
1165     Do:
1166     - Transparent on Crystal Claus, vertically standing
1167     - Crystal Claus on Transparent, vertically standing
1168     - Black black black
1169     - green
1170     - 0.2 chorm + 0.2 + 0.5 Cobolt gives strong yellow/green. Pending new weight. Pending new weight.
1171
1172     BUY:
1173     - Manganese
1174     - Nikkel
1175     - Red stain
1176
1177
1178     Do not have melt tests for:
1179         * Talc, P3345
1180         * Wollastonite, P3348
1181         * Potash Feldspar, P3296
1182         * Ball clay, P3352
1183
1184
1185         ilmenita
1186         Emanuel Cooper
1187     -->
1188 </samples>